整芯输送带
Solid Woven Conveyor Belt
带体不脱层，伸长小，抗冲击，耐撕裂，主
要用于煤矿井下。按结构不同分为PVC型、
PVG型整芯输送带。
PVG型为全塑整芯输送带。用于倾角16°以
下干燥条件的物料输送.
PVG型为橡胶面整芯输送带。用于倾角20°
以下潮湿有水物料输送。
PVC/PVG： Solid woven flame retardant belts
are used in conveying coal,without taking off for
layers,low elongation. Anti-shock and tearing resistant,usually used in mining.
resistant,usually used in mining.
PVC Belt:Used for conveying material up to 16°
inclination under dry conditions.
PVG Belt:Rubber cover,suitable for
conveying moist material up to 200 inclination
标志示例
Marks model
| MA | PVG(PVC) | 800 | S | N | 2001 | 01 |
| “安全标志”符号 Safe Marks Symbol | 覆盖层材质为橡胶 (覆盖层材质为塑料） Material of Cover:Rubber (Material of Cover:Plastic) | 阻燃带纵向拉断强度 Elongation Break Strength of Flame Retardant | 阻燃抗静电的代号 Code of Flame Retardant and Anti-static | 制造厂名称 Name of M anufacture | 制造年份 Date of Manufacture | 产品检验合格证编号Quality Certificate No. |
PVC整芯阻燃输送带
PVC整芯阻燃输送带是煤矿井下常用的输送带，其优异的安全性能得到了行业和的一致认可，现就PVC整芯阻燃输送带做一些简单的介绍。
一．PVC整芯阻燃输送带结构简介
如图所示：
如图所示：PVC整芯阻燃输送带是由整体织物芯层和表面覆盖层组成。
1．整体织物带芯层采用棉纱线和尼龙或涤纶纤维分别并股成线，然后与纬线编织叁层或叁层以上的整体织物结构后，经浸渍PVC芯糊塑化而成；
2．PVC输送带覆盖层主要由PVC盖糊涂覆塑化而成；
二．PVC整芯阻燃输送带性能特点和主要用途：
◆性能特点
1．具有优异的阻燃性良好的导电性；
2．带体不脱层、伸长小、抗冲击、耐撕裂；
3．带体轻、强力高、成槽性好
4．PVC整芯阻燃输送带适用于倾角16度以下的干燥条件下的物料输送；
◆主要用途
PVC整芯阻燃输送带因其具有良好的安全阻燃自熄性和导静电性，适用于煤矿井下易燃场合输送煤炭，如主巷道、工作采面、煤仓、洗煤厂等的煤炭输送；也可用于要求难燃导静电的电力、化工、冶金等行业。
三．技术标准
PVC整芯阻燃输送带的生产执行MT914-2008《煤矿用织物芯阻燃带》标准。
也可按BS3289、BC158、AS4606等标准组织生产。
四．产品类型及性能指标
| 产品类型 | 拉伸强度（小值） | 整体拉断伸长率 | 带宽 | 每卷带 | ||
| 纬向（N/mm） | 经向(N/mm) | 纵向 | 横向 | （mm） | 长(米) | |
| 680S/四级 | 680 | 265 | 不小于15% | 不小于18% | 400 | 50 |
| 800S/五级 | 800 | 280 | ||||
| 1000S/六级 | 1000 | 300 | ｜ | ｜ | ||
| 1250S/七级 | 1250 | 350 | ||||
| 1400S/八级 | 1400 | 350 | 2000 | 200 | ||
| 1600S/九级 | 1600 | 400 | ||||
| 1800S/十级 | 1800 | 400 | ||||
| 2000S/十一级 | 2000 | 400 | ||||
| 2240S/十二级 | 2240 | 450 | ||||
| 2500S/十三级 | 2500 | 450 | ||||
◆推荐的小滚筒直径
| 标准选型 | 推荐的小传动滚筒直径（mm） | 备 注 |
| 680S/四级 | 320 | 小滚筒直径可大一个级别选用，有利于延长输送带的使用寿命。 |
| 800S/五级 | 400 | |
| 1000S/六级 | 500 | |
| 1250S/七级 | 500 |
◆接头方式：PVC、PVG整芯阻燃输送带可机械接头也可胶粘接头。接头强度应符合以下标准：
| 型号 | 机械接头 | 胶粘接头 |
| 680S-1000S | 接头强度不小于带体额定拉伸强度的70% | 接头强度不小于带体 |
| 1250S-1600S | 接头强度不小于带体额定拉伸强度的65% | |
| 1800S-2000S | 接头强度不小于带体额定拉伸强度的60% | 额定拉伸强度的90% |
| 2000S以上 | 接头强度不小于带体额定拉伸强度的55% |
◆型号说明：例如800S，800表示阻燃带整体纵向拉伸强度为800N/mm，S表示阻燃带具有阻燃和抗静电性能。
五．生产工艺
1、高强力整体带芯
煤矿用输送带整体带芯按煤炭行业标准MT317-2002生产，经向采用涤纶或聚酯纤维和棉纱混纺，纬向受力线采用高强度、拉伸变形发性能好的尼龙纤维。提高了胶带的抗撕裂、抗冲击、面胶粘合力、抗磨损性能并有利于提高接头抗拉强度，延长阻燃带带体和接头寿命；成品带带体轻，成槽性好，节能降耗。
2、先进的挤擦式生产工艺
挤擦工艺是当前应用广、技术的PVC整芯阻燃输送带生产工艺，其生产的PVC具有耐磨、不脱层、强力高等优点,配合PVC特殊盖胶配方，在保证安全性能前提下还保持了优异的物理性能，保证了产品的防滑和耐磨性。
整芯输送带
Solid Woven Conveyor Belt
整芯输送带规格系列
Specification of Solid Woven Conveyor Belt
| 型号Type | 整体拉伸强度(N/mm) Total Tensile Strength(N/mm) | 整体拉断伸长率(％)不小于 Total Tensile Rate at Breaks≥ | 带宽(mm) Width(mm) | 每卷带长(m) Length(m)/Roll | ||
| 纵向 Longitude | 横向 Transverse | 纵向 Longitude | 横向 Transverse | |||
| 680S/ 四级(Grade 4) | 680 | 265 | 15 | 18 | 400-2000 | 50-200 |
| 800S/ 五级(Grade 5) | 800 | 280 | ||||
| 1000S/六级(Grade 6) | 1000 | 300 | ||||
| 1250S/七级(Grade 7) | 1250 | 350 | ||||
| 1400S/八级(Grade 8) | 1400 | 350 | ||||
| 1600S/九级(Grade 9) | 1600 | 400 | ||||
| 1800S/十级(Grade 10) | 1800 | 400 | ||||
| 2000S/十一级(Grade 11) | 2000 | 400 | ||||
| 2240S/十二级(Grade 12) | 2240 | 450 | ||||
| 2500S/十三级(Grade 13) | 2500 | 450 | ||||
| 2800S/十四级(Grade 14) | 2800 | 450 | ||||
| 3100S/十五级(Grade 15) | 3100 | 450 | ||||
| 3400S/十六级(Grade 16> | 3400 | 450 | ||||
织物芯输送带的执行标准主要技术指标
Standard and Main Technical Data
| 品种Type | 标准及主要指标 Standard and Main Technical Data |
| 普通型 Conventional | GB/T7984 DIN22102 |
| 耐热型 Heat Resistant | HG/T2297 T1型≤100℃ T2型≤125℃ |
| 耐高温型 High Temperature Resistant | HG/T2297 T3型≤150℃ |
| 耐烧灼型 Fire Resistant | 耐200°C以上物料烧灼 Resistant≥200°C Material Cauterize |
| 耐热磨型 Heat&Abrasion Resistant | 耐125℃，磨耗≤150mm3Resistant 125 °C,Shore Abrasion≤150mm3 |
| 耐磨型 Abrasion Resistant | 磨耗≤90mm3 Shore Abrasion≤90mm’ |
| 一般阻燃型 Conventional Flame Retardant | GB/T10822 |
| 耐寒型 Cold Resistant | 脆性温度-50℃ Fragility Temperature-50℃ |
| 耐酸、碱、盐型 Acid,Alkali,Oil Resistant | HG-846 |
| PVC PVG | BS3289 MT914 HG2805 |
整芯橡胶阻燃输送带
SWR Solid Woven Fire Resistant Belt
传统整芯带与整芯橡胶阻燃输送带的使用比较图示
Comparison between conventional and SWR solid woven belts
Performance Of Swr Solid Woven Belts
产品结构与性能对照表
Table Of Structure And Performance
| 结构与性能 Structure And Performance |
国内传统整芯带Domestic Conventional Solid Woven Belts | 国际传统整芯带 International Conventional Solid Woven Belts | 整芯橡胶阻燃输送带 SWR Solid Woven Fire Resistant Belts |
| 骨架材料 Carcass | 涤纶/锦纶+棉纱 NN/EE+CC | 涤纶/锦纶+棉纱 NN/EB-CC | 全涤纶/锦纶/芳纶 NN/EE/EP/KF |
| 覆盖层 Cover | PVC、PVG+橡胶 PVC、 PVG+Rubber |
PVC、PVG+橡胶 PVC、 PVG+Rubber |
高分子聚合物+橡胶 High Polymer+Rubber |
| 磨耗 Abrasion(mm3) | 200 | 200 | 150 |
| 覆盖层拉伸强度 Tensile Strength (Mpa) |
15 | 15 | 20 |
| 覆盖层伸长率 Elongation(%) |
350 | 350 | 400 |
| 覆盖层厚度 Cover Thickness(mm) |
5+3 | 4+2 | 12 |
| 成槽性Troughability | 一般 Fair | 良 Good | 优 Excellent |
| 同强力皮带滚筒直径 Pulley Diameter |
大 Big | 中 Medium | 小 Small |
| 生产工艺 Production Process |
带芯PVC塑化 Carcass PVC Plasticizer | 带芯PVC塑化 Carcass FVC Plasticizer | 高分子纳米体系预塑连续硫化 High Ploymer & Namo-Bonding System and Re-Plastic Continuous Vulcanization |
| 设计使用寿命Life | 1年 1year | 1_5年 1.5years | 5年 5years |